Designation by Standards
Steel No. | DIN | EN | AISI | JIS | ГОСТ |
1.3401 | X120Mn12 | - | A128 grade A | / | 110G13L |
Chemical Composition (in weight %)
C | Si | Mn | Cr | Mo | Ni | V | W | Others |
1.20 | 0.40 | 12.50 | max. 1.50 | - | - | - | - | - |
Description
Austenitic Mn-steel. The well-known Hadfield steel still has broad applications in the mineral processing industry. Especially under impact loading Hadfield steel displays good wear resistance due to its high cold work ability. However, Hadfield steel is not corrosion resistant.
Applications
Components for dredgers and crushers, conveying machines: crushings jaws, impact wedges, linings, etc.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 190-210
Density [g/cm3]: 7.88
Hardening
Harden from a temperature of 1000-1050oC followed by water quenching. Hardness after quenching is about 200 HB.
Mechnical properties at ambient temperature:
0.2 % proof stress (N/mm2): 350
Tensile strength (N/mm2): 800-1000
Forging
Hot forming temperature: 1050-850oC
Machinability
The machinability of this steel is poor.
Remark
All technical information is for reference only.