C |
Mn(2) |
Si |
Cr |
Ni(2) |
Mo |
W |
V |
Co |
Ti |
Al |
Cu |
P |
S |
Absorption of neutrons |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Scaling resistance |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Resistance to corrosion |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Cutting capacity |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Mechinability |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Red brittlenes |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Susceptibility to cracking |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Susceptibility to overheating |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Temper brittleness |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Retention of hard. by tempering |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Throught hardening (1) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Hardenability (hardness adoption by tempering |
|
|
|
|
|
|
() 3
|
() 3
|
|
|
|
|
|
|
Critical cooling rate (1) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Remanence |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Permability |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Coercitivity |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Electric resistance |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Heat conductivity |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Carbide formation |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Gamma-area |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Point A3 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Point A1 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Strengh at high temp. |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Toughness |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Elongation |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Tensile strengh |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
increases, improves |
|
x(1) |
strong dependance upon C-content |
|
reduces, worsens |
|
x(2) |
austentic steels with Ni and Mn can show a diffrent behavior |
|
strongly increases, improves |
|
x(3) |
dependent uponaustenizing temperature |
|
strongly reduces, worsens |
|
For properties, where no influence is indicated, the influence is not characteristic and/or not known.
Print this page