Designation by Standards
| Steel No. | DIN | EN | AISI | JIS | ГОСТ |
| 1.2767 | X45NiCrMo4 † | 45NiCrMo16 | - | / | / |
Chemical Composition (in weight %)
| C | Si | Mn | Cr | Mo | Ni | V | W | Others |
| 0.45 | 0.25 | 0.30 | 1.35 | 0.25 | 4.00 | - | - | - |
Description
Nickel cold work tool steel. Goof hardenability and thougness. Ability for polishing, photoetching and erosion treatment.
Applications
Forging tools, dies of all sort, shapes and sizes, hot forging and pressing tools for steel and metal. Moulds, bushings, piercers, etc.
Physical properties (avarage values) at ambient temperature
Density [g/cm3]: 7.84
Thermal conductivity [W/m.K]: 28.0
Coefficient of Linear Thermal Expansion 10-6 oC-1
| 20-100oC | 20-200oC | 20-300oC | 20-400oC | 20-500oC | 20-600oC |
| 11.7 | 12.5 | 13.0 | 13.4 | 13.7 | 13.8 |
Soft Annealing
Heat to 610-850oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 262.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to 650oC, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Harden from a temperature of 840-870oC followed by oil. air or warm bath (180-220oC) quenching. Hardness after quenching is 56 HRC.
Tempering
Tempering temperature: 150-400oC.
Tempering Temperature (oC) vs. Hardness (HRC)
| 100oC | 200oC | 300oC | 400oC | 500oC | 600oC |
| 56 | 54 | 50 | 46 | 42 | 38 |
Forging
Hot forming temperature: No data.
Machinability
No data.
Remark
All technical information is for reference only.