Designation by Standards
| Steel No. | DIN | EN | AISI |
| 1.2362 | X63CrMoV5-1 | - | - |
Chemical Composition (in weight %)
| C | Si | Mn | Cr | Mo | Ni | V | W | Others |
| 0.62 | 1.10 | 0.40 | 5.20 | 1.15 | 0.30 | - | - | - |
Description
Cr-Mo alloyed through hardening steel with high tempering resistance.
Applications
Intermediate rolls for cluster mills, trimming dies, hot cutting shears.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.81
Soft Annealing
Heat to 800-840oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 250.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to 600-650oC, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Harden from a temperature of 980-1020oC followed by oil quenching or warm bath quenching. Hardness after quenching is 61-63 HRC.
Tempering
Tempering temperature: See the data bellow.
Tempering Temperature (oC) vs. Hardness (HRC)
| 100oC | 200oC | 300oC | 400oC | 500oC | 550oC |
| 61 | 59 | 58 | 57 | 61 | 58 |
Forging
Hot forming temperature: 1100-850oC.
Machinability
No data.
Remark
All technical information is for reference only.