Steel No. DIN EN AISI JIS ГОСТ
1.4034 - X46Cr13 420 SUS420J2 40Ch13


Chemical Composition (in weight %)

C Si Mn Cr Mo Ni V W Others
0.46 max. 1.0 max. 1.0 13.50 - - - - -


Description
Steel 420 displays the best corrosion resistance in hardened condition with a surface polished to give a mirror finisih.

Applications
All kinds of cutting tools - knives, shears, surgical instruments, moulds for plastics production, as well as for surgical instruments and measuring gauges.

Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 220
Density [g/cm3]: 7.73
Thermal conductivity [W/m.K]: 30.0
Electric resistivity [Ohm mm2/m]: 0.65
Specific heat capacity[J/g.K]: 0.46

Coefficient of Linear Thermal Expansion 10-6 oC-1

20-100oC 20-200oC 20-300oC 20-400oC 20-500oC
10.5 11.0 11.0 11.5 12.0


Modulus of Elasticity [103 N/mm2]

20oC 200oC 400oC
220 205 190


Soft Annealing
Heat to 730-780oC, cool slowly in furnace or air. Structure is ferrite with spherical carbides.

Hardening
Harden from a temperature of 980-1030oC followed by oilor air quenching. Hardness after quenching is 56 HRC.

Tempering
Tempering temperature: 100-200oC.

Tempering Temperature (oC) vs. Hardness (HRC)

20oC 100oC 200oC 300oC 400oC 500oC 600oC
56 56 55 52 51 52 42


Forging
Hot forming temperature: 1100-800oC.

Machinability
Similar to machining some of the high carbon tool steel, this alloy has tough, stringy chip build-up.

Corrosion Resistance
420 is resistant to the atmosphere, fresh water, dilute acids and alkalis and fruit and vegetable juices.

Welding
Not commonly welded due to its air hardening characteristics. Welding may be performed after preheating to 149-204oC with post weld tempering at temperature for 2 hours . Filler metal should be AWS E/ER420.

Note: The hot forming temperature stated should not be exceeed, as harmful grain coarsening and simultaneous formation of a carbide network along the grain boundaries will otherwise occur. This results in poor developmnet of hardness and a decline in toughness and elasticity in hardened condition.

Remark
All technical information is for reference only.